The influence of biaxial loading on branching of a dissolution driven stress corrosion crack
Stress corrosion cracking occurs due to the synergistic interaction between mechanical load and corrosion reactions. In this study, branching during anodic dissolution driven crack growth is studied using an adaptive FE procedure. The crack has an inherent blunt tip due to the dissolution, and the growth is treated as a moving boundary problem with a strain-assisted evolution law. Simulations are